Pelapisan Calsium Carbida Permukaan Baja Karbon Rendah Dengan Pack Carburizing Energizer Serbuk Cangkang Kerang Mutiara
DOI:
10.29303/jpft.v6i2.2073Diterbitkan:
2020-12-14Terbitan:
Vol 6 No 2 (2020): Juli-DesemberKata Kunci:
low carbon steel, pack carburizer, media carburize, pinctada maxima shell powderArticles
Unduhan
Cara Mengutip
Unduhan
Metrik
Abstrak
The research was conducted at the Laboratory of Material Mechanics, Department of Mechanical Engineering, Mataram University. The purpose of this researchààdeterminedàthe effect of the Pack Carburizingàparameters (temperature, soakinàtime and carburizer media composition) on the thicknessàof calsium carbida layerà(CaC), which is formed on the surface of low carbon steel. The thickness of the calcium carbonate layer affects the surface hardness numberàof low carbon steel. This research used low carbon steelàgrade SS400 as the specimen. Carburizer media is a mixture of corncob charcoal powder and Pinctada maxima shellsàpowder (PMSP).àPacks Carburizing was carried out at various temperatures: 875 0C, 900 0C, soakingàtime: 1,2,3 hours and the percentage of PMSP on the carburizer media: 10%, 20%, 30%. The results of the research show that the temperature carburizing , soaking time and the addition of PMSPàaffect the thickness of the calcium carbide layer on the surface of SS400 steel which is subjected to pack carburizing process. This is indicated by an increase in the surfaceàhardness number of 421%, the wear resistance 62,2 %. àthe thickness of the calcium carbide layer 1050 õm, the formation of pearlite structure, at the carburizing temperature of 900 0C,àsoaking time 3 hours and 30% addition of PMSP.
Referensi
William D. Callister. (2014). Materials Science and Engineering 9th Edition John Wiley.
Ihom, P. A. (2013). Case hardening of mild steel using cowbone as Energiser. African Journal of Engineering Research, 1(October), 97ââ¬â101.
Jatmiko, B. A. (2013). Karburisasi Baja SS316 Menggunakan Arang Sekam Padi Dan Arang Kayu Sengon. Skripsi. Tidak dipublikasikan. Bogor: Departemen Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Institut Pertanian Bogor
Khadijah, S., Abdullah, B., Jaffar, A., Abdul, S., Faizul, M., Azimin, M., & Ghani, A. (2013). Mechanical properties of paste carburized ASTM A516 Steel. Procedia Engineering, 68, 525ââ¬â530. https://doi.org/10.1016/j.proeng.2013.12.216
Kuswanto, B. (2010). Pengaruh Perbedaan Ukuran Butir Arang Tempurung Kelapa-Barium Karbonat Terhadap Peningkatan Kekerasan Permukaan Material Baja ST 37 Dengan Proses Pack Carburizing. Tesis. Tidak dipublikasikan. Semarang: Magister Teknik Mesin Program Pascasarjana Universitas Diponegoro.
Miernik, K., Bogucki, R., & Pytel, S. (2010). Effect of Quenching Techniques on The Mechanical Properties of Low Carbon Structural Steel. Archives of Foundry Engineering, 10(3), 91ââ¬â96.
Ngakan, D., & Putra, K. (2016). Efektifitas Carburizer dari Sumber Karbon Berbeda Pada Proses Pack Carburizing. METTEK, 2(1), 5ââ¬â10.
Oyetunji, A., & Adeosun, S. O. (2012). Effects of Carburizing Process Variables on Mechanical and Chemical Properties of Carburized Mild Steel. Pakistan Journal of Basic and Applied Sciences, 8(2), 1ââ¬â7.
Priyadarshini, S., Sharma, T., & Arora, G. (2014). Effect of Post Carburizing Treatment on Hardness of Low Carbon Steel. International Journal of Advanced Mechanical Engineering, 4(7), 763ââ¬â766. Retrieved from http://www.ripublication.com
Rai, P. K. (2016). Study on Mechanical Properties of Carburized Mild Steel Subjected to Heat Treatment. International Journal of Engineering Technology and Computer Research (IJETCR), 4(1), 83ââ¬â87.
Rijab, M. A., & Al-mosawi, A. I. (2014). Effect of carburizing on fatigue strength. In 3rd International Scientific Conference F.T.E.
Roy, S., & Sundararajan, S. (2016). Surface & Coatings Technology The effect of heat treatment routes on the retained austenite and Tribomechanical properties of carburized AISI 8620 steel. Surface & Coatings Technology, 308, 236ââ¬â243. https://doi.org/10.1016/j.surfcoat.2016.06.095
Sujita Darmo, Rudy Soenoko, Eko Siswanto And Teguh Dwi Widodo, (2018). Study On Mechanical Properties Of Pack Carburizing SS400 Steel With Energizer Pomacea Canalikulata Lamarck Shell Powder. International Journal of Mechanical Engineering and Technology (IJMET) - Scope Database Indexed.Volume:9,Issue:5,Pages:14-23. Available online at http://www.iaeme.com/ijmet/issues.asp?JType=IJMET&VType=9&IType=5.
Sujita Darmo, Rudy Soenoko, Eko Siswanto And Teguh Dwi Widodo, (2018). Study Pack Carburizing For Subsoil Plow Chisel With Alternative Carburizer Media Corn Cob Charcoalââ¬âPictada Maxima Shell Powder. International Journal of Mechanical Engineering and Technology (IJMET) - Scope Data base Indexed.Volume:9,Issue:6,Pages:443-449. Available online at http://www.iaeme.com/ijmet/issues.asp?JType=IJMET&VType=9&IType=6
Biografi Penulis
Sujita Darmo, Universitas Mataram
Sugiman Sugiman, Universitas Mataram
Salman Salman, Universitas Mataram
Agus Dwi Catur, Universitas Mataram
Paryanto Dwi Setyawan, Universitas Mataram
Lisensi
Penulis yang menerbitkan Jurnal Pendidikan Fisika dan Teknologi (JPFT) setuju dengan ketentuan sebagai berikut:
- Penulis memiliki hak cipta dan memberikan hak jurnal untuk publikasi pertama dengan karya yang dilisensikan secara bersamaan di bawah Lisensi Internasional Creative Commons Attribution-ShareAlike License 4.0 (Lisensi CC-BY-SA). Lisensi ini memungkinkan penulis untuk menggunakan semua artikel, kumpulan data, grafik, dan lampiran dalam aplikasi penambangan data, mesin pencari, situs web, blog, dan platform lain dengan memberikan referensi yang sesuai. Jurnal memungkinkan penulis untuk memegang hak cipta tanpa batasan dan akan mempertahankan hak penerbitan tanpa batasan.
- Penulis dapat membuat pengaturan kontrak tambahan yang terpisah untuk distribusi non-eksklusif dari versi jurnal yang diterbitkan dari karya tersebut (misalnya, mempostingnya ke penyimpanan institusional atau menerbitkannya dalam sebuah buku), dengan pengakuan atas publikasi awalnya di Jurnal Pendidikan Fisika dan Teknologi (JPFT).
- Penulis diizinkan dan didorong untuk memposting karya mereka secara online (misalnya, di repositori institusional atau di situs web mereka) sebelum dan selama proses pengiriman, karena hal itu dapat mengarah pada pertukaran yang produktif, serta kutipan yang lebih awal dan lebih besar dari karya yang diterbitkan (Lihat The Pengaruh Akses Terbuka).